JOMINY HARDENABILITY TEST. Objective. To study hardness as a function of quench rate and investigate the hardenability of steels. Introduction. PDF | The Jominy end-quench test is used to measure the hardenability of a steel , which is a measure of the capacity of the steel to harden in depth under a. The Jominy end-quench test is used to measure the hardenability of a steel, which is a measure of the capacity of the steel to harden in depth.

Author: Vijora Shaktijin
Country: Central African Republic
Language: English (Spanish)
Genre: Sex
Published (Last): 7 May 2018
Pages: 470
PDF File Size: 16.22 Mb
ePub File Size: 11.25 Mb
ISBN: 351-1-21298-212-3
Downloads: 65079
Price: Free* [*Free Regsitration Required]
Uploader: Zolohn

For example, any video clips and answers to questions are missing. The formatting page breaks, etc of the printed version is unpredictable and highly dependent on your browser. The Jominy end quench test is used to measure the hardenability of a steel, which is a measure of the capacity of the steel to harden in depth under a given set of conditions. This TLP considers the basic concepts of hardenability and the Jominy test. Knowledge about the hardenability of steels is necessary to be able to select the appropriate combination of alloy steel and heat treatment to manufacture components of different size to minimize thermal stresses and distortion.

The Jominy end quench test is the rest method for measuring the hardenability of steels. This describes the ability of the steel to be hardened in depth by quenching. Hardenability depends hardenaability the chemical composition of the steel and also be can affected by prior processing conditions, such as the austenitizing temperature. It is not only necessary to understand the basic information provided from the Jominy test, but also to appreciate how the information obtained can be used to understand the effects of alloying in steels ojminy the steel microstructure.

Hardenability is the ability of a steel to partially or completely transform from austenite to some fraction of martensite at a given depth below the surface, when cooled under a given condition.

For example, a steel of a high hardenability can transform to a high fraction of martensite to depths of several millimetres under relatively slow cooling, such as an oil quench, whereas a steel of low hardenability may only form a high fraction of martensite to a depth of less than jomint millimetre, even under rapid cooling such as a water quench.

Hardenability therefore describes the capacity of the steel to harden in depth under a given set of conditions. Steels with high hardenability are needed for large high strength components, such as large extruder screws for injection moulding of polymers, pistons for rock breakers, mine shaft supports, aircraft undercarriages, and also for harfenability high precision components such as die-casting moulds, drills and presses for stamping coins.

High hardenability allows slower quenches to be used e. Steels with low hardenability may be used for smaller components, such as chisels and shears, or for surface hardened components such as gears. The steel sample is normalised to eliminate differences in microstructure due to previous forging, and then austenitised. The test sample is quickly transferred to tet test machine, where it is held vertically and sprayed with a controlled flow of water onto one jominny of the sample.

This cools the specimen from one end, simulating the effect of quenching a larger steel component in water. The cooling rate varies hadenability the length of the sample from very rapid at the quenched end, to rates equivalent to air cooling at the other end. The round specimen is then ground flat along its length to a depth of 0. The hardness iominy measured hardenabilityy intervals from the quenched end. The interval is typically 1.

High hardness occurs where high volume fractions of martensite develop. Similar tests have been developed in other countries, such as the SAC test, which uses a sample quenched from all sides by immersion in water.

This is commonly used in the USA. It is then trst and quickly moved to the quenching machine and positioned above a water jet. The water jet is started and sprayed onto the bottom of the specimen until the specimen is cool. Your browser does not support the video tag. As the water jet sprays onto the end of the hot, glowing specimen, a cold dark region spreads up the specimen.

  AP GODSE DIGITAL ELECTRONICS PDF

Jominy End Quench Test

The hardenabilith region has transformed from austenite to a mixture of martensite, ferrite and pearlite. The proportions of the phases at any position depends on the cooling rate, with more martensite formed where the cooling rate is fastest.

Ferrite and pearlite are formed where the cooling rate is slower. This alternative longer video clip contributed joominy Oxford Brookes University shows both the transfer of the sample from furnace to Hradenability machine, and the jet spraying one end of the sample. Data from the Jominy end quench test can be used to determine whether a particular steel can be sufficiently hardened in different quenching media, for different section diameters.

For example, the cooling rate at a distance of 9. A high hardenability is required for through hardening of large components. This data can be presented using CCT C ontinuous C ooling T ransformation diagrams which are used to select steels to suit the component size and quenching media.

Slow quenching speeds are often chosen to reduce distortion and residual stress in components. Slower cooling rates hardeability at the core of larger uominy, compared to hardejability faster cooling rate at the surface. In the example here, the surface will be transformed to martensite, but the core will have a hardenabi,ity structure with some martensite. Jominy end quench test can also be used to demonstrate the effects of microstructure and alloying variables on the hardenability of steels.

These include alloying elements and grain size. The main alloying elements which affect hardenability are carbon, boron and a group of elements including Cr, Mn, Mo, Si and Ni. Carbon controls the hardness of the martensite. Increasing the carbon content increases the hardness of steels up to about 0. At higher carbon levels, the formation of martensite is depressed to lower temperatures and the transformation from austenite to martensite may be incomplete, leading to retained austenite.

This composite microstructure of martensite and austenite gives a lower hardness to the steel, although the microhardness of the martensite phase itself is still high. However, the effect is too small be be commonly used for control of hardenability. High carbon steels are prone to distortion and cracking during harenability treatment, and can be difficult to machine in the annealed condition before heat treatment. It is more common to control hardenability with other elements, and to use carbon levels of less than 0.

Boron is a very potent alloying element, typically fest 0. The effect of boron is also independent of the amount of boron, provided sufficient is added, and the effect of boron is greatest at lower carbon contents.

It is typically used with lower carbon steels. Boron has a very strong affinity for oxygen and nitrogen, with which it forms compounds. Boron can therefore only affect the hardenability of steels if it is in solution. This requires the addition of “gettering” elements such as aluminium and titanium to react preferentially with the oxygen and nitrogen in the steel.

The most commonly used elements are Cr, Mo and Mn. The retardation is due to hardeanbility need for redistribution of the alloying elements during the diffusional phase transformation from austenite to ferrite and pearlite. The solubility of the elements varies between the different phases, and the interface between the growing phase cannot move hardebability diffusion of the slowly moving elements.

There are quite complex interactions between the different elements, which also affect the temperatures of the phase transformation and the resultant microstructure. Steel compositions are sometimes described in terms of a carbon tesg which describes the magnitude of the effect of all of the elements on hardenability. Increasing the austenite grain size increases the hardenability of steels.

The nucleation of ferrite and pearlite occurs at heterogeneous nucleation sites such as the austenite grain boundaries. Increasing the austenite grain size therefore decreases the available nucleation sites, which retards the rate of the phase transformation.

This method of increasing the hardenability is rarely used since haedenability increases in hardenability require large austenite grain size, obtained through high austenitisation temperatures.

  LAS MEDIDAS Y LOS HOMBRES WITOLD KULA PDF

The resultant microstructure is quite coarse, with reduced toughness and ductility. The austenite grain size can be affected by other stages in the hhardenability of steel, and therefore the hardenability of a steel also depends on the previous stages employed in its production. Example Jominy end quench test data A plain carbon steel and an alloy tezt were assessed using the Jominy end quench test. The hardness harednability the samples was measured as a function of the distance from the quenched end to demonstrate the different hardenability of the two steels.

The data is shown as Vickers and Rockwell hardness. The Vickers hardness test uses a square pyramidal diamond indentor. The recorded hardness depends on the indentation load and the width of the kominy indentation made by the diamond. The hardness number is usually denoted by HV20 for H ardness V ickers 20 kg, for example. The Vickers test is most commonly used in the UK.

The Rockwell hardness of a metal can also be determined using a similar technique. The variation of hardness was measured with distance from the quenched end. The results are plotted in the graph below. Click on the circled data points to see how the microstructure varies with distance from the quenched end. The alloy steel clearly has the highest hardenability, forming martensite to a greater depth than the plain carbon steel. Look at both the microstructures at high magnification, and try to observe the relationship between the volume fraction of martensite and the hardness of the steel.

The Rockwell hardness test measures a number which depends on the difference in hardenabilit depth of an indentation made by two jo,iny, a minor load followed by a major load.

The Jominy End Quench Test, ASTM A

There are different scales for the Rockwell hardness test. The indentor is either a conical diamond pyramid, or a hardened steel ball. The Rockwell test is commonly used in the USA. There are conversion charts between the hardness scales. It’s important to use the correct conversion chart for different materials, since the hardness test causes plastic strain, and therefore varies with the strain hardening properties of the material.

The graph below gives the Jominy end quench data in terms of the Rockwell hardness number. Clicking on the circled data points will take you to images of the microstructure at that location in the sample. In this heat flow simulation you can adjust various parameters and observe the effect on the heat flow and cooling of the specimen. The simulation ignores the effect of heat loss from the sides of the specimen, i.

The bar is divided into 25 equal gest elements, and, at each time step of the simulation, for each element, a new temperature, resulting from heat transfer at either end, is calculated.

Hardenahility size of the time step is set to the maximum allowed while ensuring numerical stability of the simulation.

This animation requires Adobe Flash Player 8 and later, which can be downloaded here. The Jominy Test involves heating a test piece from the steel 25mm diameter and mm long to an austenitising temperature and quenching from one end with a controlled and standardised jet of water.

Take a sample from the furnace and place it on the Jominy test fixtures and observe the cooling pattern. After quenching the hardness profile is measured at intervals from the quenched harenability after the surface has been ground back to remove any effects of decarburisation 0. The hardness variation along the test surface is a result of microstructural variation which arises since the cooling rate decreases with distance from the quenched end.

The hardenability depends on the alloy composition of the steel, and can also be affected by prior processing, such as the austenitisation temperature. Knowledge of the hardenability of steels is necessary in order to select the appropriate combination of alloy and heat treatment for components of different size, to minimise thermal stresses and distortion.